168 results
Now showing 1 - 10 of 168
- PublicationMicrostructure and wear characteristics of nickel based hardfacing alloys deposited by plasma transferred arc welding(01-08-2006)
;Gurumoorthy, K.; ;Rao, K. P.Venugopal, S.In the present investigation, a nickel based hardfacing alloy (AWS NiCr-B) was deposited on an austenitic stainless steel substrate 316LN using the plasma transferred arc welding process. The deposit was characterised by hardness measurements, microstructural examination and sliding wear assessment. Identification of precipitates was carried out using X-ray diffraction and SEM/ EDAX. These studies revealed the presence of chromium rich carbides and borides in a γ-Ni matrix. Down to a distance of 1 mm from the interface, the hardness of the deposit was found to be 52 HRC. The sliding wear behaviour of the hardfacing alloy was investigated in air in the room temperature to 550°C range, with a pin on disk configuration using a cylindrical pin with tip radius of 3 mm under loads of 30, 40 and 50 N. Wear experiments were conducted up to a sliding distance of 180 m at a sliding speed of 0-1 m s -1. The elastic modulus and Poisson's ratio of the hardfaced deposits were evaluated by the ultrasonic method and these values were used for calculating initial Hertzian contact stress. The study showed that, while significant wear loss occurred at room temperature, there was practically no measurable weight loss at temperatures of 300 and 550°C. This could be attributed to the formation of an oxide layer at the surface during wear testing. © 2006 Institute of Materials, Minerals and Mining. - PublicationDamage characterization of unmodified and surface modified medical grade titanium alloys under fretting fatigue condition(25-01-2006)
;Vadiraj, AravindFretting is a form of adhesive wear normally occurring at the contact points gradually leading to premature of load bearing medical implants made of titanium alloys. The aim of this work is to characterize the fretting fatigue damage features of PVD TiN coated, plasma nitrided and thermally oxidized Ti-6Al-4V and Ti-6Al-7Nb contact pairs. Fretting damage is applied with calibrated proof ring and contact pad arrangement. The results are compared with fretting damage of uncoated alloys. The damage progression during fretting process is apparently explained with friction coefficient curves. Plasma nitrided pairs performed better in terms of fretting fatigue lives with low friction coefficient of friction. PVD TiN coated pairs have experienced early failures due to third body mode of contact interaction with irregular friction coefficient pattern. Thermally oxidized pairs have experienced early failures due to high case thickness as well as irregular development of modified layer. © 2005 Elsevier B.V. All rights reserved. - PublicationMicrostructure and mechanical properties of 9Cr-1Mo steel weld fusion zones as a function of weld metal composition(01-11-2009)
;Arivazhagan, B. ;Prabhu, Ranganath ;Albert, S. K.; Sundaresan, S.Modified 9Cr-1Mo steel, designated as P91, is widely used in the construction of power plants and other sectors involving temperatures higher than 500 °C. Although the creep strength is the prime consideration for elevated temperature applications, notch toughness is also important, especially for welded components, as it is essential to meet the pressure test and other requirements at room temperature. P91 steel weld fusion zone toughness depends on factors such as welding process, chemical composition, and flux composition. Niobium and vanadium are the main alloying elements that significantly influence the toughness as well as creep strength. In the current work, weld metals were produced with varying amounts of niobium and vanadium by dissimilar joints involving P9 and P91 base metals as well as filler materials. Microstructural studies and Charpy V-notch impact testing were carried out on welds to understand the factors influencing toughness. Based on the results, it can be concluded that by reducing vanadium and niobium weld metal toughness can be improved. © ASM International. - PublicationEffect of scanning speed, nozzle stand-off distance and beam scan-off distance on coating properties of laser surface alloyed 13Cr-4Ni steel(01-01-2008)
;Shivamurthy, R. C.; ; ;Shariff, S. M.Padmanabham, G.The present work describes an investigation of the effect of 3 different parameters of laser surface alloying-i.e., laser scanning speed (LSS), nozzle stand-off distance (NSOD) and laser beam scan-off distance (LBSOD) on coating height, depth and width. Nickel-based Colmonoy 88 alloy powder has' been deposited on 13Cr-4Ni steel by single-step process of laser surface alloying. Laser power and powder feed rate were maintained at 3kW and 25 g/min, respectively. L8 orthogonal array has been designed to study these 3 parameters at 2 levels each. The results of single pass with extent of dilution, surface hardness and microstructures produced by different conditions are presented and discussed. For a specified NSOD and LBSOD, there was a decrease in coating height and depth with increase in LSS. Coating height and depth were not affected much by increase in NSOD. From the present investigation, optimized parameters were identified for enhanced hardness, minimum dilution and desired coating height and coating depth. - PublicationEffect of weld cooling rate on Laves phase formation in Inconel 718 fusion zone(01-01-2014)
;Manikandan, S. G.K. ;Sivakumar, D. ;Rao, K. PrasadInconel 718 (2 mm thick) was welded using argon and helium gas shielded tungsten arc welding process with a filler metal. Both constant current and compound current pulse modes were applied and the cooling rates calculated. The dependence of Laves phase formation, dendrite arm spacing and niobium segregation ratios in fusion zone on the nature of shielding gases and current was studied. The maximum instantaneous weld cooling rate was achieved for the combination of Helium shielding gas and compound current pulse mode. This ultimately resulted in reduction of laves phase, segregation of niobium and dendrite arm spacing in the fusion zone. © 2013 Elsevier B.V. All rights reserved. - PublicationMicrostructural aspects of plasma transferred arc surfaced Ni-based hardfacing alloy(15-05-2007)
;Gurumoorthy, K.; ;Rao, K. Prasad ;Rao, A. SambasivaVenugopal, S.In the current investigation, nickel-base hardfacing alloy AWS NiCr-B was deposited on austenitic stainless steel substrate 316 LN using the plasma transferred arc-welding process. The deposit was characterized by hardness measurements, microstructural examination and sliding wear assessment. Identification of precipitates was carried out using X-ray diffraction, scanning electron microscope/energy dispersive X-ray analysis (SEM/EDAX), electron probe micro analyzer (EPMA) mappings and line-scan profiles. The microstructure of the hardfacing deposit predominantly consists of the γ-Ni phase and the interdendritic eutectic mixture comprised of γ-nickel and nickel-rich borides. These studies also revealed the presence of chromium-rich carbides and borides in a γ-nickel matrix. The sliding wear behaviour of the hardfacing alloy was investigated in air at three different temperatures viz., room temperature, 300 and 500 °C. The study revealed significant weight loss at room temperature and abrupt decrease at high temperatures. This behaviour at high temperatures has been attributed to the formation of a wear protective oxide layer at the surface during sliding. To evaluate the microstructural stability of the deposit, ageing studies were carried out at 650 °C for 250 h. Microstructural examination and hardness testing revealed that there is no deterioration in the microstructure and that the hardness remains intact. Sliding wear tests at room temperature and at high temperatures also demonstrated that there is no significant change in the weight loss or the wear behaviour after the thermal exposure. © 2007 Elsevier B.V. All rights reserved. - PublicationFretting wear studies on uncoated, plasma nitrided and laser nitrided biomedical titanium alloys(15-02-2007)
;Vadiraj, Aravind; Fretting wear resistance of uncoated and surface modified biomedical titanium alloys (Ti-6Al-7Nb) in air and Ringer fluid has been investigated in the present work. Laser nitrided specimen has shown superior performance with minimum surface damage and wear rate (<0.1 × 10-6 mm3/Nm) despite high friction coefficient in air (0.6) compared to uncoated and plasma nitrided (>12 × 10-6 mm3/Nm) specimens. This is due to presence of TiN dendrites (60-80%) in the laser nitrided layer. Plasma nitrided surface is relatively softer and hence wear rates and surface damage are comparable with uncoated alloys. Friction coefficient is high for uncoated (0.8) and plasma nitrided alloys (0.6) in air as well as Ringer fluid. Fretting induced electrochemical dissolution is responsible for higher wear rates in uncoated and plasma nitrided specimens. The fretting damage resistance is primarily governed by relative hardness and modified layer thickness of the mating components. © 2006 Elsevier B.V. All rights reserved. - PublicationEffect of TIG arc surface melting process on weld metal toughness of modified 9Cr-1Mo (P91) steel(30-06-2008)
;Arivazhagan, B. ;Sundaresan, S.Modified 9Cr-1Mo steel is widely used in the construction of power plants. Flux-shielded processes result in inadequate weld metal toughness due to the presence of inclusions. An acidic-coated electrode with primary constituent of rutile in flux coating tends to produce inferior toughness due to the presence of coarse microinclusions in the resultant weld. In the present study, welds produced using acidic-coated electrodes were given a surface melting using TIG process to refine the inclusions. There was significant reduction in number of coarse microinclusions and increase in number of fine microinclusions. Charpy V-notch test was conducted at room temperature to evaluate the toughness of weld. Surface melted welds have superior toughness compared to unmelted welds. Fractographic features correlate well with the observed impact energy values of welds. © 2008 Elsevier B.V. All rights reserved. - PublicationInfluence of aging treatment on microstructure, wear and corrosion behavior of a nickel base hardfaced coating(03-10-2011)
;Kesavan, D.In this work nickel based hardfacing alloy (Colmonoy 5) was deposited on 316L (N) stainless steel substrate to study the effects of aging treatment on coating microstructure, wear and corrosion properties. Coatings, deposited through plasma transferred arc (PTA) welding process, were aged at 923K for 5000h. Microstructural characterization studies carried out by scanning electron microscopy (SEM) and transmission electron microscopy (TEM) revealed the coarsening of dendrites and precipitation of Cr23C6 particles in the aged coating. The wear behavior of the as deposited and aged coatings was compared in room temperature (RT) and high temperature (823K) under dry sliding wear condition (pin-on-disc configuration). At RT, aged coating experienced more wear loss when compared to as-deposited. At high temperature, the wear loss was almost same with similar operating wear mechanisms (tribo-oxidation) for both as-deposited and aged coating. From pitting corrosion studies, it was found that aged coatings are more prone to pitting when compared to the as-deposited coatings. © 2011 Elsevier B.V. - PublicationRole of nanocrystalline feedstock in the tribological behaviour of alumina coatings deposited by detonation gun(01-11-2012)
;Manojkumar, P. A. ;Gandhi, A. S.; ;Thomas Paul, V. ;Kumar, N.Tyagi, A. K.Alumina coatings were prepared using detonation gun from commercial powder (CP) and high energy ball milled powder (MP) with 83 nm crystallite size. The sliding wear rate and wear coefficient of friction were lower in the nanocrystalline powder coating. The coating from the as-received commercial powder consisted of thick splats, and a paucity of nanoparticulate inter-splat regions whereas milled powder coating has thinner splat morphology with nanoparticulate inter-splat regions. The nanoparticulate material in the inter-splat regions and the finer microstructure of the MP coating is believed to be responsible for improved wear resistance. © 2012 Elsevier Ltd. All rights reserved.