Magnetic and magnetocaloric properties of nanocrystalline Pr1 <inf>x</inf>A <inf>x</inf>Mn <inf>1</inf> yCo <inf>y</inf>O <inf>3</inf> (A = Ca, Sr) (x = 0.3; y = 0.5) manganites

Structural, magnetic and magnetocaloric properties of sol-gel prepared, nanocrystalline oxides Pr 1-xA xMn1-yCo yO 3 (A = Ca, Sr) (x = 0.3; y = 0.5) (cubic, space group Fm3̄m) have been studied. From the X-ray data, the crystallite size of Pr 0.7Ca 0.3Mn 0.5Co 0.5O 3 and Pr 0.7Sr 0.3Mn 0.5Co 0.5O 3 samples is found to be ∼24 nm and ∼15 nm respectively. High resolution transmission electron microscopy image shows average particle size of ∼34 nm and ∼20 nm. Magnetization measurements indicate a Curie temperature of ∼153 K and ∼172 K in applied magnetic field of 100 Oe for Pr 0.7Ca 0.3Mn 0.5Co 0.5O 3 and Pr 0.7Sr 0.3Mn 0.5Co 0.5O 3 compounds. The magnetization versus applied magnetic field curves obtained at temperatures below 150 K show significant hysteresis and magnetization is not saturated even in a field of 7 T. The magnetocaloric effect is calculated from M versus H data obtained at various temperatures. Magnetic entropy change shows a maximum near T C for both the samples and is of the order ∼2.5 J/kg/K. © 2011 American Scientific Publishers.