Spectral, mechanical, thermal, optical and solid state parameters, of metal-organic bis(hydrogenmaleate)-CO(II) tetrahydrate crystal

Metal-organic bis(hydrogenmaleate)-Co(II) tetrahydrate single crystals have been grown by slow evaporation solution growth technique at room temperature. The crystal structure and the unit cell parameters were analyzed from the X-ray diffraction studies. Single-crystal X-ray diffraction analyses reveal that the grown crystal belongs to triclinic system with the space group P-1. Functional groups in bis(hydrogenmaleate)-Co(II) tetrahydrate were identified by Fourier transform infrared spectral analysis. The peak observed at 663 cm^-1 is assigned to the (Co-O) stretching vibrations. The optical transmission of the crystal was studied by UV-vis-NIR spectral analysis. The photoluminescence emission studies were carried out for the title compound in a wide wavelength range between 350 nm and 550 nm at 303 K. Mechanical strength was tested by Vickers microhardness test. The laser damage threshold value has been determined using Nd:YAG laser operating at 1064 nm. At various frequencies and temperatures the dielectric behavior of the material was investigated. Solid state parameters such as plasma energy, Penn gap, Fermi energy and electronic polarizability were evaluated. Photoconductivity measurements were carried out for the grown crystal in the presence of DC electric field at room temperature. Thermal stability and decomposition of the crystal were studied by TG-DTA. The weight loss of the title compound occurs in different steps.