Diffuse phase transition of Fe doped lead ytterbium tantalate ceramics

The effect of different concentration of Fe on the phase transition behavior of Lead ytterbium tantalate is investigated by dielectric and differential scanning calrimetry measurements. The samples are prepared through solid state reaction method and it has been found that the sintering temperature significantly lowered when the proportion of Pb(Fe1/2Ta 1/2)O3 increased. It has been observed that the doping in small amounts (0≤x≤0.2) of Fe could meliorate the dielectric and ferroelectric properties. The diffuseness in the mode of phase transition increases and the phase transition temperature decreases as a function of Fe content. It is revealed that the dielectric data and heat capacity data follow a similar trend in the variation of the mode of phase transition and phase transition temperatures. The phase transition temperature values obtained from the heat capacity measurement well agreed with the values obtained from dielectric measurement. © 2005 Elsevier Ltd. All rights reserved.