Creep deformation of induction pressure welded 2·25Cr-1Mo steel

In this paper, experimental results involving the effect of stress and temperature on creep behaviour of induction pressure welded (IPW) 2·25Cr-1Mo steel are presented. Creep rupture tests were conducted at 550-700°C in steps of 50°C over a stress range of 112·5-180 MPa. Above 650°C failure of the specimen was enhanced due to the microstructural instability. Failure in the specimens occurred invariably in the heat affected zones (HAZ), and the fracture surfaces indicated ductile failure. © 1994.