On material removal mechanism in high speed single grit scratchgrinding of cryo-treated Al2024-T351 aluminium alloy

Feasibility of utilizing cryogenic technology to improve the shearability of Al2024-T351 alloy is experimentally investigated by carrying out a single grit scratch-grinding test. A single grit brazed diamond grinding tool is developed for the study. Al2024-T351 work specimens are treated with liquid nitrogen for 6 hours before the scratch test. Although there was no significant change in the tensile strength of the material, the surface experiences change in the microhardness. It helps in arresting the side flow and ploughing of the material during high speed scratch grinding. The scratched grooves on cryo-treated samples, compare to those of untreated specimens, shows signs of cleaner shear-cuts, superior finish and produces less grinding force during grinding.